Glass-ceramics can be versatile joining materials with tailorable thermal and mechanical properties; they are not affected by oxidation and can be used as pressureless joining materials above their glass softening point. The glassy phase can be minimized by a suitable thermal treatment in order to improve the glass-ceramic creep behaviour. The use of glasses and glass-ceramics as sealants in solid oxide fuel cells and as joining materials for SiC-based materials will be discussed.